Pengaruh Jenis Laminasi terhadap Kuat Tarik dan Perubahan Warna pada Pressure sensitive label PE White
DOI:
https://doi.org/10.59024/jisi.v4i3.1981Keywords:
Glossy Lamination, Matte Lamination, Polyethylene White, Pressure-Sensitive Label, Tensile StrengthAbstract
Pressure sensitive labels (PSLs) made of polyethylene (PE) white are widely used in the packaging industry due to their flexibility, moisture resistance, and ease of application on various substrates. This study aimed to examine the effect of glossy and matte lamination on the tensile strength and color difference (ΔE) of PE white PSLs. An experimental method was employed, with tensile testing conducted using a universal testing machine (UTM) in accordance with ASTM standards and color measurement performed using a spectrodensitometer based on the CIE Lab system. The samples were divided into three treatment groups, namely no lamination, glossy lamination, and matte lamination, with ink coverage controlled at two design conditions, full ink and minim ink. The results indicated that lamination type significantly affected both the mechanical and visual characteristics of the labels. In the tensile strength test, the highest mean value was obtained by one treatment group, indicating superior resistance to tensile loading. In terms of color stability, higher ΔE values indicated greater color change and lower lightfastness, whereas lower ΔE values reflected better color retention. Overall, the findings show that the combination of lamination type and ink coverage influences the performance of PE white PSLs in both mechanical strength and color stability.
References
Andrade, C. (2024). Understanding Factorial Designs, Main Effects, and Interaction Effects: Simply Explained with a Worked Example. Indian Journal of Psychological Medicine, 46(2), 175–177. https://doi.org/10.1177/02537176241237066
Clarke, B. R., Hu, X., Petek, E., Witt, C. L., Katsumata, R., Watkins, J. J., Crosby, A. J., & Tew, G. N. (2025). Wet/Dry Bottlebrush Pressure Sensitive Adhesives via a Dangling Defect-Driven Design. ACS Applied Materials and Interfaces, 17(20), 30140–30148. https://doi.org/10.1021/acsami.5c05934
de Castro, L. D. C., Engels, T. A. P., Oliveira, O. N., & Schenning, A. P. H. J. (2024). Sticky Multicolor Mechanochromic Labels. ACS Applied Materials and Interfaces, 16(11), 14144–14151. https://doi.org/10.1021/acsami.3c19420
Feng, T., Chen, H., & Zhang, M. (2023). Applicability and Freshness Control of pH-Sensitive Intelligent Label in Cool Chain Transportation of Vegetables. Foods, 12(18). https://doi.org/10.3390/foods12183489
Fitzgerald, D. M., Colson, Y. L., & Grinstaff, M. W. (2023). Synthetic pressure sensitive adhesives for biomedical applications. In Progress in Polymer Science (Vol. 142). Elsevier Ltd. https://doi.org/10.1016/j.progpolymsci.2023.101692
Jeon, J., Kim, J., Park, S., Bryan, G., Broderick, T. J., Stone, M., & Tsukruk, V. V. (2024). Double-Sided Pressure-sensitive Adhesive Materials under Human-Centric Extreme Environments. ACS Applied Materials and Interfaces, 16(36), 48257–48268. https://doi.org/10.1021/acsami.4c09327
Jha, A., Gryska, S., Barrios, C., & Frechette, J. (2024). Adhesion and Contact Aging of Acrylic Pressure-sensitive Adhesives to Swollen Elastomers. Langmuir, 40(8), 4267–4276. https://doi.org/10.1021/acs.langmuir.3c03413
Jiang, C., Liu, G., Zhang, Q., Wang, S., & Zou, Y. (2024). Preparation and characterization of intelligent packaging labels based on pea starch, κ-carrageenan and black raspberry extract for monitoring freshness of pork. Food Chemistry: X, 24. https://doi.org/10.1016/j.fochx.2024.101850
Kulčar, R., Maretić, D., & Vukoje, M. (n.d.). Introduction DYNAMICS OF THERMOCHROMIC COLOR CHANGE OF PRESSURE SENSITIVE LABELS FACESTOCK MADE FROM ENVIRONMENTALLY FRIENDLY MATERIALS. Retrieved https://raconteur.uberrip.com/i/1289441-future-of-packaging-2020/13?m4=
Luo, W., Chen, W., Liu, D., Huang, X., & Ma, B. (2024). Effect of temperature and humidity on mechanical properties and constitutive modeling of pressure-sensitive adhesives. Scientific Reports, 14(1). https://doi.org/10.1038/s41598-024-64960-2
Mozelewska, K., & Antosik, A. K. (2022). Influence of Silicone Additives on the Properties of Pressure-sensitive Adhesives. Materials, 15(16). https://doi.org/10.3390/ma15165713
N, J., Ahmed, N., & Rattan, R. (2023). Evaluation and Assessment of the Colour Stability of Modified Polymethyl Methacrylate Denture Base Materials and Polyether Ether Ketone in a Cast Partial Denture Framework: An In-Vitro Study. Cureus. https://doi.org/10.7759/cureus.48189
Naffah, N., Ounsi, H., Ozcan, M., & Salameh, Z. (2024). Evaluation of the Color Stability of Three Resin-Ceramic Materials Using a Spectrophotometer and a Digital Photography Software. Contemporary Clinical Dentistry, 15(1), 44–50. https://doi.org/10.4103/ccd.ccd_656_18
Ortega-Iguña, M., Chludzinski, M., & Sánchez-Amaya, J. M. (2022). Comparative Mechanical Study of Pressure Sensitive Adhesives over Aluminium Substrates for Industrial Applications. Polymers, 14(21). https://doi.org/10.3390/polym14214783
Park, K. H., Lee, D. Y., Yoon, S. H., Kim, S. H., Han, M. S., Jeon, S., Kim, Y., Lim, Y. K., Hwang, D. H., Jung, S. H., & Lim, B. (2022). Adhesion Improvement of Solvent-Free Pressure-sensitive Adhesives by Semi-IPN Using Polyurethanes and Acrylic Polymers. Polymers, 14(19). https://doi.org/10.3390/polym14193963
Poloni, E., Rafsanjani, A., Place, V., Ferretti, D., & Studart, A. R. (2022). Stretchable Soft Composites with Strain-Induced Architectured Color. Advanced Materials, 34(6). https://doi.org/10.1002/adma.202104874
Schmiedt, R., Krainz, M., Tosic, K., Sharbafian, F., Krauter, S., Krauter, V., Novak, M., Rainer, B., Washüttl, M., & Apprich, S. (2025). Impact of EVOH, Ormocer® Coating, and Printed Labels on the Recyclability of Polypropylene for Packaging Applications. Polymers, 17(24). https://doi.org/10.3390/polym17243332
Singh, P., Maiti, S., & Shenoy, A. (2024). Comparative evaluation of bond strength and color stability of polyetheretherketone and zirconia layered with indirect composite before and after thermocycling: An in vitro study. Journal of Indian Prosthodontic Society, 24(3), 252–258. https://doi.org/10.4103/jips.jips_36_24
Wang, G., Wang, S., Hu, T., & Shi, F. (2024). Multifunctional Hydrogel with 3D Printability, Fluorescence, Biodegradability, and Biocompatibility for Biomedical Microrobots. Molecules, 29(14). https://doi.org/10.3390/molecules29143351
Xue, W., Zhang, X., Sun, C., Wei, C., Zhang, L., Yang, H., & Wang, R. (2025). Biobased Itaconate Acrylic Pressure-sensitive Adhesives via Emulsion Polymerization: Sustainable Design for High Peel Resistance. ACS Omega, 10(37), 42494–42506. https://doi.org/10.1021/acsomega.5c03586
Downloads
Published
Issue
Section
License
Copyright (c) 2026 JURNAL ILMIAH TEKNIK INDUSTRI DAN INOVASI
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.